FORMULATED FOR SHALLOW-TO-MEDIUM DEPTH WELLS AND/OR LIGHT-TO-MODERATE ROD LOADS
The grade C sucker rod is manufactured from modified UNS G15360 carbon steel. After normalizing and tempering with specially selected temperatures to maximize impact properties, all rods are shot peened per our own unique standards, developed to significantly improve corrosion and fatigue resistance. Recommended for reciprocating rod lift applications, the grade C sucker rod is designed to maximize performance and improve runtime in fluids that are effectively inhibited to prevent corrosion. Grade C sucker rods are not recommended for use in Progressing Cavity Pumping (PCP) applications.
MADE IN AMERICA
LUFKIN Rods is the only privately owned and operated Sucker Rod manufacturing plant in the USA. All our products are sourced and manufactured domestically, and our advanced manufacturing plant ensures the highest quality possible. Our automated systems continually monitor the manufacturing process and ensures the quality is consistent from start to finish. Throughout the entire manufacturing process, our quality control is unmatched in the industry to meet the needs of our customers’ most demanding well conditions. LUFKIN Rods will help you meet or exceed your production goals, and can offer expert help with predictive designs, product selection, failure analysis, training and much more. Put our experienced team to work for you and let us help you reduce your failure rates and improve your bottom line.
SPECIFICATIONS
- UNS Series Steel
- G15360
- End Cap Color
- White
- Carbon, %
- 0.34 to 0.39
- Manganese, %
- 1.15 to 1.35
- Phosphorus, %
- 0.04 max.
- Sulfur, %
- 0.04 max.
- Silicon, %
- 0.15 to 0.35
- Nickel, %
- 0.25 max.
- Chromium, %
- 0.20 max.
- Molybdenum, %
- 0.06 max.
- Vanadium, %
- 0.04 to 0.07
- Copper, %
- 0.35 max.
- Yield Strength, 2-inch offset, psi
- 60,000 min.
- Tensile Strength, psi
- 90,000 to 115,000
- Elongation, 8-inches, %
- 13 min.
- Reduction of Area, %
- 45 min.